Silicate-based, breathable paint for interiors
Puro_titanium & VOC Free is a water-based matt mineral paint for interiors, formulated with polysilicate of potassium, odorless and without biocides, volatile organic compounds (VOC) and Formaldehyde.
Puro_titanium & VOC Free sensitively reduces the formaldehyde concentration in the surrounding environment, as tested per the specific law ISO 16000-23.
Puro_titanium & VOC Free represents the expression of Novacolor commitment to the environmental sustainability. To reduce the “carbon footprint”, Puro_titanium & VOC Free is formulated with a special binder, made from sustainable biomass, that replaces the fossil raw materials.
This is possible thanks to a technical-productive system called “mass balance approach” certified REDcert2.
It contains an innovative mix of mineral charges that guarantee hiding without the use of Titanium dioxide.
Its innovative formulation makes Puro_titanium & VOC Free suitable for the application on each kind of walls, mineral or synthetic paints, and direct application on plasterboard. The high breathability and alkaline nature help to preserve the substrate from mold development.
Application:
- The substrate must be perfectly dry, dust-free, with no humidity and salt stains.
- Resurface or consolidate the surface with specific products if necessary.
- In case of mould, treat the surface with suitable specific products. Brush or remove any efflorescence and old peeling paint.
- Higher layers of old lime-based paint and tempera paint must be removed. Brush out dust, smog or other deposits before the application.
- In case of chalky and non-homogeneous surfaces, apply a layer of Zer0 Primer (mineral water-based primer) using a brush.
- Over dry substrate, apply the first layer of Puro_titanium & VOC Free with roller, brush or airless.
- Once the substrate is completely dry, generally in 4 hours, apply a second layer of Puro_titanium & VOC Free with roller, brush or airless.
- Drying time: 24 hours approx. depending on the kind of substrate, absorption rate and environmental conditions.
May also be applied over:
- New and old base hydraulic binder-based plaster.
- Concrete surfaces.
- Gypsum and plasterboard surfaces
- Old paints and organic or mineral coatings, dry, compact, absorbent and cohesive.
- Various absorbent mineral conglomerates.
Approximate coverage yields 5-6 m2/l in two layers for applications on smooth and absorbent substrates. It is recommend a preliminary test on the specific substrate to verify the effective yield.